EPALINE 795 A 15 15

EPALINE 795 A 15 15 is a polyether based thermoplastic polyurethane, with excellent physical and mechanical properties, superior resistance to hydrolysis and microbial attack, very good low temperature flexibility and very good wear resistance.
We recommend using EPALINE 795 A 15 15 in extrusion processes, such as production of hoses, tubes, cables and 3D filaments. It can also be used for injection molding.

Property	Norm	Value	Unit
Density	ISO 1183-1 ASTM D 792	1,14 1.14	g/cm³ g/cm³
Hardness (5 sec.)	ISO 7619 ASTM D 2240	93 93	Shore A Shore A
Tensile stress at 50% elongation	EN 527-1 ASTM D 412	8,8 1500	MPa psi
Tensile stress at 100% elongation	EN 527-1 ASTM D 412	11,1 1800	MPa psi
Tensile stress at 300% elongation	EN 527-1 ASTM D 412	20,9 3500	MPa psi
Tensile strength	EN 527-1 ASTM D 412	45 5400	MPa psi
Elongation @ break	EN 527-1 ASTM D 412	450 450	% %
Tear strength	ISO 34-1; B ASTM D 624	120 650	N/mm pli
Abrasion	ISO 4649 ISO 4649	30 30	mm³ mm³
MFI rate 210°C / 5kg	ISO 1133 ISO 1133	25 25	g/10min g/10min

Values shown are based on testing of laboratory test specimens, conditioned at 70°C for 14 hours, and represent data that fall within the standard range of properties for the natural material. They are not intended for use in establishing maxiumum, minimum or range of values for specification purpose.

Material preparation

EPALINE 795 A 15 15 is hygroscopic and therefore has to be dried before use. The recommended drying conditions are 2-3 hours at 80 - 90°C in a desiccant dryer.