EPAMOULD 292 A 30

EPAMOULD 292 A 30 is a polyester based thermoplastic polyurethane with excellent physical and mechanical properties, resistance to oils and greases, improved hydrolysis resistance, high crystallisation rate and very good wear resistance.
We recommend using EPAMOULD 292 A 30 for injection molding processes, such as production of technical parts.

Property	Norm	Value	Unit
Density	ISO 1183-1 ASTM D 792	1,21 1.21	g/cm³ g/cm³
Hardness (5 sec.)	ISO 7619 ASTM D 2240	92 92	Shore A Shore A
Tensile stress at 50% elongation	EN 527-1 ASTM D 412	7,6 1200	MPa psi
Tensile stress at 100% elongation	EN 527-1 ASTM D 412	8,8 1400	MPa psi
Tensile stress at 300% elongation	EN 527-1 ASTM D 412	19,9 2900	MPa psi
Tensile strength	EN 527-1 ASTM D 412	50 5700	MPa psi
Elongation @ break	EN 527-1 ASTM D 412	430 590	% %
Tear strength	ISO 34-1; B ASTM D 624	125 610	N/mm pli
Abrasion	ISO 4649 ISO 4649	25 25	mm³ mm³
MFI rate 205°C / 5kg	ISO 1133 ISO 1133	10 10	g/10min g/10min

Values shown are based on testing of laboratory test specimens, conditioned at 70°C for 14 hours, and represent data that fall within the standard range of properties for the natural material. They are not intended for use in establishing maxiumum, minimum or range of values for specification purpose.

Material preparation

EPAMOULD 292 A 30 is hygroscopic and therefore has to be dried before use. The recommended drying conditions are 2-3 hours at 80 - 90°C in a desiccant dryer.