EPAMOULD 660 A 26 E

EPAMOULD 660 A 26 E is a polyester based thermoplastic polyurethane with excellent physical and mechanical properties, resistance to oils and greases, very short cycle times and perfect adhesion with most PU systems.
We recommend using EPAMOULD 660 A 26 E for injection molding processes, such as production of technical parts. It can also be used in extrusion.

Property	Norm	Value	Unit
Density	ISO 1183-1 ASTM D 792	1,18	g/cm³ g/cm³
Hardness (5 sec.)	ISO 7619 ASTM D 2240	71	Shore A Shore A
Tensile stress at 50% elongation	EN 527-1 ASTM D 412	2,5	MPa psi
Tensile stress at 100% elongation	EN 527-1 ASTM D 412	3,4	MPa psi
Tensile stress at 300% elongation	EN 527-1 ASTM D 412	8,0	MPa psi
Tensile strength	EN 527-1 ASTM D 412	25	MPa psi
Elongation @ break	EN 527-1 ASTM D 412	650	% %
Tear strength	ISO 34-1; B ASTM D 624	65	N/mm pli
Abrasion	ISO 4649 ISO 4649	60	mm³ mm³
MFI rate 180°C / 5 kg	ISO 1133 ISO 1133	15	g/10min g/10min

Values shown are based on testing of laboratory test specimens, conditioned at 70°C for 14 hours, and represent data that fall within the standard range of properties for the natural material. They are not intended for use in establishing maxiumum, minimum or range of values for specification purpose.

Material preparation

EPAMOULD 660 A 26 E is hygroscopic and therefore has to be dried before use. The recommended drying conditions are 2-3 hours at 70 - 80°C in a desiccant dryer.