EPAMOULD 752 D 35

EPAMOULD 752 D 35 is a polyether based thermoplastic polyurethane, with excellent physical and mechanical properties, superior resistance to hydrolysis and microbial attack, good transparency, very good low temperature flexibility and wear resistance.
We recommend using EPAMOULD 752 D 35 for injection molding processes, such as production of technical parts.

Property	Norm	Value	Unit
Density	ISO 1183-1 ASTM D 792	1.17 42370	g/cm³ g/cm³
Hardness (5 sec.)	ISO 7619 ASTM D 2240	50 50	Shore D Shore D
Tensile stress at 50% elongation	EN 527-1 ASTM D 412	14.3 2100	MPa psi
Tensile stress at 100% elongation	EN 527-1 ASTM D 412	16.8 2500	MPa psi
Tensile stress at 300% elongation	EN 527-1 ASTM D 412	33.2 4100	MPa psi
Tensile strength	EN 527-1 ASTM D 412	50 6000	MPa psi
Elongation @ break	EN 527-1 ASTM D 412	400 450	% %
Tear strength	ISO 34-1; B ASTM D 624	145 850	N/mm pli
Abrasion	ISO 4649 ISO 4649	40 40	mm³ mm³
MFI rate 225°C / 5kg	ISO 1133 ISO 1133	45 45	g/10min g/10min

Values shown are based on testing of laboratory test specimens, conditioned at 70°C for 14 hours, and represent data that fall within the standard range of properties for the natural material. They are not intended for use in establishing maxiumum, minimum or range of values for specification purpose.

Material preparation

EPAMOULD 752 D 35 is hygroscopic and therefore has to be dried before use. The recommended drying conditions are 2-3 hours at 210 - 230°F in a desiccant dryer.