EPALINE 395 A 55 25

EPALINE 395 A 55 25 is a polyester based thermoplastic polyurethane with excellent physical and mechanical properties, resistance to oils and greases and very good wear resistance.
We recommend using EPALINE 395 A 55 25 in extrusion processes, such as production of hoses, tubes and 3D filaments. It can also be used for injection molding.

Property	Norm	Value	Unit
Density	ISO 1183-1 ASTM D 792	1,2 1.20	g/cm³ g/cm³
Hardness (5 sec.)	ISO 7619 ASTM D 2240	94 94	Shore A Shore A
Tensile stress at 50% elongation	EN 527-1 ASTM D 412	10,0 1500	MPa psi
Tensile stress at 100% elongation	EN 527-1 ASTM D 412	11,1 1750	MPa psi
Tensile stress at 300% elongation	EN 527-1 ASTM D 412	26,9 3600	MPa psi
Tensile strength	EN 527-1 ASTM D 412	50 5900	MPa psi
Elongation @ break	EN 527-1 ASTM D 412	450 460	% %
Tear strength	ISO 34-1; B ASTM D 624	130 650	N/mm pli
Abrasion	ISO 4649 ISO 4649	25 25	mm³ mm³
MFI rate 210°C / 5kg	ISO 1133 ISO 1133	20 20	g/10min g/10min

Material preparation

EPALINE 395 A 55 25 is hygroscopic and therefore has to be dried before use. The recommended drying conditions are 2-3 hours at 80 - 90°C in a desiccant dryer.