EPALINE 785 A 15 15 M

EPALINE 785 A 15 15 M is a polyether based thermoplastic polyurethane, with excellent physical and mechanical properties, superior resistance to hydrolysis and microbial attack, very good low temperature flexibility, very good wear resistance and matt surface.
We recommend using EPALINE 785 A 15 15 M in extrusion processes, such as production of hoses and tubes. It can also be used for injection molding.

Property	Norm	Value	Unit
Density	ISO 1183-1 ASTM D 792	1,11 1.11	g/cm³ g/cm³
Hardness (5 sec.)	ISO 7619 ASTM D 2240	86 86	Shore A Shore A
Tensile stress at 50% elongation	EN 527-1 ASTM D 412	5,8 900	MPa psi
Tensile stress at 100% elongation	EN 527-1 ASTM D 412	6,8 1000	MPa psi
Tensile stress at 300% elongation	EN 527-1 ASTM D 412	10,3 1600	MPa psi
Tensile strength	EN 527-1 ASTM D 412	38 4000	MPa psi
Elongation @ break	EN 527-1 ASTM D 412	620 600	% %
Tear strength	ISO 34-1; B ASTM D 624	80 400	N/mm pli
Abrasion	ISO 4649 ISO 4649	45 45	mm³ mm³
MFI rate 200°C / 5kg	ISO 1133 ISO 1133	20 20	g/10min g/10min

Values shown are based on testing of laboratory test specimens, conditioned at 70°C for 14 hours, and represent data that fall within the standard range of properties for the natural material. They are not intended for use in establishing maxiumum, minimum or range of values for specification purpose.

Material preparation

EPALINE 785 A 15 15 M is hygroscopic and therefore has to be dried before use. The recommended drying conditions are 2-3 hours at 80 - 90°C in a desiccant dryer.