EPAMOULD 255 D 10

EPAMOULD 255 D 10 is a polyester based thermoplastic polyurethane with excellent physical and mechanical properties and improved hydrolysis resistance.
We recommend using EPAMOULD 255 D 10 for injection molding processes, such as production of technical parts and footwear components.

Property	Norm	Value	Unit
Density	ISO 1183-1 ASTM D 792	1.23	g/cm³ g/cm³
Hardness (5 sec.)	ISO 7619 ASTM D 2240	97	Shore A Shore A
Hardness (5 sec.)	ISO 7619 ASTM D 2240	58	Shore D Shore D
Tensile stress at 50% elongation	EN 527-1 ASTM D 412	18,5	MPa psi
Tensile stress at 100% elongation	EN 527-1 ASTM D 412	20,9	MPa psi
Tensile stress at 300% elongation	EN 527-1 ASTM D 412	41,2	MPa psi
Tensile strength	EN 527-1 ASTM D 412	50	MPa psi
Elongation @ break	EN 527-1 ASTM D 412	300	% %
Tear strength	ISO 34-1; B ASTM D 624	150	N/mm pli
Abrasion	ISO 4649 ISO 4649	30	mm³ mm³
MFI rate 220°C / 5 kg	ISO 1133 ISO 1133	20	g/10min g/10min

Material preparation

EPAMOULD 255 D 10 is hygroscopic and therefore has to be dried before use. The recommended drying conditions are 2-3 hours at 100 - 110°C in a desiccant dryer.