EPAMOULD 85 H S

EPAMOULD 85 H S is a polyester based thermoplastic polyurethane with good transparency, improved hydrolysis resistance, resistance to oils and greases, good physical properties and wear resistance.
We recommend using EPAMOULD 85 H S for injection molding processes, such as production of footwear components and technical parts.

Property	Norm	Value	Unit
Density	ISO 1183-1 ASTM D 792	1,20	g/cm³ g/cm³
Hardness (5 sec.)	ISO 7619 ASTM D 2240	85	Shore A Shore A
Tensile stress at 50% elongation	EN 527-1 ASTM D 412	5,0	MPa psi
Tensile stress at 100% elongation	EN 527-1 ASTM D 412	6,2	MPa psi
Tensile stress at 300% elongation	EN 527-1 ASTM D 412	16,1	MPa psi
Tensile strength	EN 527-1 ASTM D 412	40	MPa psi
Elongation @ break	EN 527-1 ASTM D 412	450	% %
Tear strength	ISO 34-1; B ASTM D 624	100	N/mm pli
Abrasion	ISO 4649 ISO 4649	35	mm³ mm³
MFI rate 205°C / 5 kg	ISO 1133 ISO 1133	20	g/10min g/10min

Values shown are based on testing of laboratory test specimens, conditioned at 70°C for 14 hours, and represent data that fall within the standard range of properties for the natural material. They are not intended for use in establishing maxiumum, minimum or range of values for specification purpose.

Material preparation

EPAMOULD 85 H S is hygroscopic and therefore has to be dried before use. The recommended drying conditions are 2-3 hours at 70 - 80°C in a desiccant dryer.